| MATERIAL A | MATERIAL B | ||
| POLY-354A | ISO-1002 | ||
Parameter | Value | Value | Unit |
Apperance at room temperature | White milky | Yellow transparent | - |
Melting point | -10℃ | 0℃ | ℃ |
Solid material melting time | 0-1 | 0-1 | hours |
Viscosity at 35 。C | 1500 | 400 | mPa·s |
Density at working temperature | 1.1 | 1.05 | g/cm³ |
Mixing ratio | 100 | 75-80 | V/m |
Working temperature | 45 | 40 | ℃ |
Moulds temperature | 45-55 | ℃ | |
Demoulding time Reaction performance | 180-240 | second | |
(Cream Time/Thread Time) | 7-9 | second | |
Free Density | 0.19-0.24 | g/cm³ | |
Parameter | Value | Unit |
Density(UNI 10902) | 0.35-0.38 | g/cm³ |
Hardness (UNI EN ISO 868) | 40-45 | Shore A |
Elogation at break(UNI EN 12803) | 300 | % |
Tensile strength at break (UNI 12803) | 8 | MPa |
Tear Resistance(UNI EN 12771) | 30 | N/mm |
Abrasion resistance (UNI EN 12770) | 200 | mg |
Flexural fatigue resistance(UNI EN ISO 17707) Test temperature:+23℃ without original hole |
100000 |
Flex time |
*It is based on test results from samples taken on 10mm plates using Derkim Polyurethane test methods in our laboratories. *It is recommended that our products be stored at room temperature in places that are not exposed to direct sunlight and rain. | ||